不锈钢酸洗污泥对烧结黏结相与平衡相的影响

 不锈钢酸洗污泥安全填埋占用土地且难以消除对环境的危害，将酸洗污泥作为烧结配料使用有望回收其中铁、铬、镍等金属，并充分利用其中的熔剂组分，实现酸洗污泥在冶金企业的闭路资源化利用。铁矿粉配加酸洗污泥烧结黏结相强度试验表明，随着酸洗污泥配加比例的增加，黏结相强度先增加后减小，且随着碱度的增加整体减小，当酸洗污泥配加比例为10%时，试样中赤铁矿、磁铁矿质量分数最大，枪晶石质量分数较小，在碱度为1.5时于1 280 ℃焙烧4 min，试样的黏结相强度最大可达15.12 kN。平衡相烧结试验表明，配加酸洗污泥能改善烧结矿质量，铁矿粉配加10%的酸洗污泥，碱度为1.5，1 300 ℃烧结240 min后，烧结矿的矿相组成和微观结构最好，综合性能最佳。     

Electromagnetic torque detecting for optimization of in-mould electromagnetic stirring in the billet and bloom continuous casting

ABSTRACT

In this paper, an electromagnetic torque device based on the theoretical model was established to determine the optimum frequency accurately and conveniently in billet and bloom continuous casting with in-mould electromagnetic stirring (M-EMS). Magnetic characteristics with M-EMS was investigated by numerical simulation and physical experiment with the application of electromagnetic torque device and gauss meter. In addition, the effects of stirring frequency with M-EMS on macro segregation and equiaxed crystal ratio were compared and analysed for 55SiCr with 150?mm?×?150?mm billet caster and BU with 310?×?360?mm bloom caster by a series of plant trials, respectively. The results showed that maximum magnetic flux density and maximum electromagnetic torque occurred with different frequency and same current in M-EMS, and central equiaxed crystal ratio and macro segregation has been significantly improved by optimum frequency with M-EMS.     

P91、P92坯料扩氢退火工艺研究

根据挤压坯料扩氢退火理论,试验优化了P91、P92坯料的扩氢退火工艺曲线,退火时间明显下降,坯料退火后的H含量大幅降低,低倍无白点缺陷,退火组织均匀,各项技术指标满足工艺要求。     

钢包包衬侵蚀对内衬温度和钢水温降的影响

为了研究包衬侵蚀对钢水温降的影响规律,通过ANSYS有限元软件以及ParaMesh网格随移技术建立了考虑包衬侵蚀的钢包传热计算模型,研究并分析了包衬侵蚀对包衬及钢水温度的影响规律。结果表明,包衬侵蚀对包衬温度影响较大,在相邻两个修包周期内,包衬侵蚀造成渣线和包壁的包衬内部(工作层与永久层交界处)温差为14～114 K;包衬侵蚀导致包壳外表面温度升高,包壳向外散热增加,与此同时,包衬受侵蚀变薄,蓄热减少,两者同时作用导致包衬侵蚀对钢水温降影响不大,最高不超过1 K,在实际生产中可以适当地忽略钢包侵蚀对钢水温降的影响。     

Lipids and Antiplatelet Therapy: Important Considerations and Future Perspectives

Lipids play an essential role in platelet functions. It is known that polyunsaturated fatty acids play a role in increasing platelet reactivity and that the prothrombotic phenotype plays a crucial role in the occurrence of major adverse cardiovascular events. The ongoing increase in cardiovascular diseases’ incidence emphasizes the importance of research linking lipids and platelet function. In particular, the rebound phenomenon that accompanies discontinuation of clopidogrel in patients receiving dual antiplatelet therapy has been associated with changes in the lipid profile. Our many years of research underline the importance of reduced HDL values for the risk of such a rebound effect and the occurrence of thromboembolic events. Lipids are otherwise a heterogeneous group of molecules, and their signaling molecules are not deposited but formed “on-demand” in the cell. On the other hand, exosomes transmit lipid signals between cells, and the profile of such changes can be monitored by lipidomics. Changes in the lipid profile are organ-specific and may indicate new drug action targets.     

Effect of spheroidized microstructure on the impact toughness and electrochemical performance of a high-carbon steel

The influence of cementite spheroidization on the impact toughness and electrochemical properties of a high-carbon steel has been thoroughly investigated in this study. Heavy warm rolling, followed by 2 h of annealing, has resulted in near-complete spheroidization, leading to a microstructure consisting of nano-cementite globules dispersed in the ultrafine-grained ferritic matrix. The Charpy impact test exhibited superior impact toughness with increased spheroidization. It is validated by the presence of abundant dimples in the fractographs of spheroidized specimens, in contrast to the as-received one that experienced a brittle failure due to its lamellar pearlitic structure. Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) carried out in a 3.5% NaCl solution revealed that the corrosion resistance of the alloy gets improved with the increase in the degree of spheroidization. This is attributed to the lower susceptibility of the spheroidized specimen to microgalvanic corrosion owing to the minimum area of contact between nano-spheroidized cementite and ferrite, as elucidated with the help of EIS results aided by equivalent electrical circuit model.     

42CrMo钢加热过程中的奥氏体晶粒尺寸演变

通过金相试验方法测定42CrMo钢在890~930 ℃下保温10~240 min后的晶粒尺寸。结果表明,42CrMo钢在加热到试验温度890~930 ℃时已经完全奥氏体化,保温过程中的晶粒生长属于正常生长;加热温度对晶粒尺寸的影响较大,保温时间对晶粒尺寸的影响较小;随保温时间的延长晶粒生长缓慢,晶粒尺寸与保温时间满足指数小于1的函数关系。基于试验数据,通过线性回归得到晶粒长大的Beck模型参数,通过非线性回归得到Sellars和Anelli模型参数,3个模型的预测精度都较好,而Anelli模型的适用性要高于Beck模型和Sellars模型,故在预测42CrMo钢的奥氏体晶粒长大规律时宜使用Anelli模型。     

Corrosion behaviors of carbon steel induced by life activities of Phaeodactylum tricornutum in a marine environment

Microbiologically influenced corrosion induced by bacteria has been studied for many years. Corrosion is known to be sensitive to the presence of microalgae, such as Phaeodactylum tricornutum. However, the life activity of P. tricornutum that influences the general and localized corrosion of carbon steel is not fully understood. The current study uses a combination of immersion tests and electrochemical experiments with a detailed surface characterization to reveal the naturally formed corrosion products with/without the presence of P. tricornutum. The results show that samples suffer from pitting corrosion and the averaged pit depths are approximately 15 μm under a light–dark cycle condition or a 24-h constant light condition. Meanwhile, the corrosion products are mainly comprised of γ-FeOOH and Fe₃O₄ in a constant light condition. However, γ-FeOOH, Fe₃O₄, and FeCO₃ are found in a light–dark cycle. This study proposes the fundamental mechanisms of the effect of P. tricornutum life activities on the corrosion performance of Q235 carbon steel, to fulfill the knowledge gaps of the presence of microalgae inducing the general and pitting corrosion of carbon steel.